英语释义

1. the temperature at which a change in phase occurs also the limiting temperature of a transformation range

片语

transformation spot temperature转变点温度

ferrite transformation actual temperature铁素体相变实际转变温度

transformation temperature of brittleness脆性转变温度

transformation temperature ranges转变温度区

Transformation Temperature Correction相变点修正

Lorentz transformation of temperature温度Lorentz变换

transformation of temperature温度变换

brittle ductility transformation temperature脆

英汉例句

• underpure argon the transformation temperature is higher than under pure hydrogen.

  在纯氩中这一转变温度要比在纯氢中高。

• differential thermal analysis (dta) tests were used to measure the effect of nitrogen on phase transformation temperature of primary austenite of fe-c-si and fe-c-si-mn grey cast irons.

  灰铸铁初生奥氏体析出温度的影响，并运用热力学原理对实验结果进行了讨论。

• the transformation temperature of every sample is attained by dta approach.

  利用示差热分析方法（dta）分析了各试样相变温度；

• the thermal analysis was used to determine the crystallization temperature, the glass transformation temperature and low temperature relaxation temperature of the amorphous samples.

  通过对非晶态样品的热分析，确定了它的晶化温度、玻璃转变温度和低温弛豫温度。

• the effect of nb on structure at elevated temperature and phase transformation temperature of chilled cast iron was studied in this paper.

  采用高温金相显微镜研究了含铌冷硬铸铁高温的金相组织，差热分析仪测定了铌对冷硬铸铁固态相变温度的影响。

• the results indicate that the austenitic transformation temperature of the deposited metal of w110 wire is 692~779 ℃, δ-ferrite exists in 1330~1468 ℃, the solid and liquid phase lines is 1371~1468 ℃.

  结果表明，该焊丝熔敷金属的奥氏体转变温度为692～779 ℃，在1330～1468 ℃温度区间存在高温铁素体相，固液相温度区间为1371～1468 ℃；

• iron and zinc doping can lower the transformation temperature of anatase to rutile.

  铁及锌的掺杂会降低锐钛晶向金红石的转变温度。

• the phase transformation temperature was very important to titanium and its alloys.

  相变温度对钛及钛合金加工和热处理来说具有重要意义。

• the reason of the difference of phase transformation temperature between different titanium alloys was discussed.

  并分析了不同钛合金之间相变点差异的原因。

• the results show that the eutectic transformation temperature of gray iron decreases with the increase of antimony content.

  结果表明，随着锑含量的增加，灰口铁共晶转变温度降低；

• the effect regularity of annealing and aging processes on the r, m transformation temperature and temperature hysteresis were given out.

  （摩尔分数）形状记忆合金丝相变特性的影响，给出了退火、时效工艺对该合金r、m相变温度和热滞的影响规律。

• the calculation method of transformation temperature and volume fraction are given. conparing with common accepted method, the obtained by this method results were more close to experimental results.

  与普遍采用的计算相变行为的方法相比较，用此方法得到的计算机模拟结果与实验结果吻合得更好。

• results show that the critical nucleus will be reduced and the initial transformation temperature of ferrite improved with increase of the deformation store energy.

  计算表明，变形能的加入可以使临界核胚减小，并且提高铁素体开始转变的温度。

• the invention relates to a method of measuring transformation temperature of liposome, belonging to the analysis measuring field.

  本发明属于分析测试领域，具体是涉及一种测定脂质体相变温度的方法。

• microstructure observation shows that the fired part was ever heated to transformation temperature which made the well-frame undergo a normalization.

  金相组织分析判断火烧部位曾进入到相变温度，使原来为退火状态的井架底部进行了一次不充分正火。

• ce can increase the transformation temperature of bainite and enlarge intervals of bainite.

  铈会使贝氏体转变点升高， 同时加大了贝氏体转变间隔；

• the effect of transformation temperature of weld metal on the residual stresses and the fatigue strength of welded joints is analyzed based on their test.

  通过焊缝金属相变温度和残余应力测试以及焊接接头疲劳强度试验，分析了焊缝金属相变温度对焊接残余应力和焊接接头疲劳强度的影响规律。

• the doping of co, ag, w can lower the transformation temperature of anatase to rutile.

  的掺杂会降低锐钛矿相向金红石相的转变温度。

• the c-re segregation lowers the transformation temperature of pearlite, which lessens the thickness of lamellas and lamellar spacing of pearlite and induces the granular pearlite.

  re偏聚使珠光体转变的开始温度降低，从而减小珠光体的片层厚度及层间距，并导致粒状珠光体的形成。

• pearlite transformation temperature after control-rolling was measured by a pressure-dilatometer for high-carbon steels under conditions of continuous cooling.

  采用压力-膨胀仪测定了高碳钢经控制轧制后，在连续冷却下珠光体的相变温度；