英语释义

1. white iron sense 2

片语

alloy white cast iron合金白口铸铁

RE white cast iron稀土白口铁

manganiferous white cast iron含锰白口铸铁

white e cast iron白口铁

Hypoeutectic White Cast Iron亚共晶白口铸铁

white cast iron cas白口铸铁

manganese white cast iron锰白口铸铁

white iron白口铸铁；白心铁

resistant white cast iron高效抗磨白口铸铁

Tungalloy white cast iron钨白口铸铁

英汉例句

• the results show that the modified abrasion resistant medium chrome white cast iron can successfully be applied to slurry pumps which should work under medium or medium-high wear duties.

  结果表明：经化学成分调整后中铬抗磨白口铸铁可成功用于生产中等或中等稍强磨损工况下使用的渣浆泵，成本低，耐磨性优良。

• the effect of v on nodulizing of carbides was observed in the as-cast, nomalized and oil quenched condition in low cr white cast iron alloyed with v.

  在低铬白口铸铁的基础上加入钒，观察钒含量对碳化物的团球化影响。

• the effect of inoculation on the structure and properties of jhigh- chromium white cast iron is investigated in this paper.

  研究了孕育对铬白口铸铁组织及性能的影响。

• a kind of new wearresistance cast iron was researched by means of adding tiny alloys to white cast iron with the high hardness and wearresisatance .

  在硬度高、耐磨性好的白口铸铁的基础上，加入多种合金元素而获得一种新型抗磨铸铁。

• based on the analysis of the effect of excitation force of vibration aging on the fatigue life of white cast iron parts, the selection gist for excitation force was determined.

  从理论上分析了振动时效激振力对白口铸铁工件疲劳寿命的影响，确定了白口铸铁疲劳破坏工件振动时效激振力的选择依据。

• variation and failure of the grinding ball of high chromium white cast iron during production and service are mainly caused by the internal stress.

  内应力是造成高铬白口铸铁磨球在生产和服役过程中出现变异和失效的主要原因。

• the improvement of white cast iron integrated mechanical property by inoculation and heat treatment is suggested.

  本文提出了一种改善白口铸铁综合机械性能的方法——变质处理和热处理。

• considering practical use conditions, technology design principle of producing low chrome white cast iron grinding ball should be:under premise of improving toughness, to enhance hardness more.

  前言：考虑磨料介质的实际服役工况条件，生产低铬白口铸铁磨球的工艺设计原则应明确为：在改善韧性指标的前提下，进一步提高硬度。

• the microstructure and mechanical properties of a new type wear-resistant white cast iron with the boride as wear-resistant phase were investigated.

  研究以硼化物为耐磨相的新型耐磨白口铸铁的组织特点与力学性能。

• the carbides types, techniques preparation, microstructure, property, and applications range of three kinds of chromium white cast iron were introduced.

  分析了三种铬系白口铸铁的碳化物类型、制备工艺、组织形貌、性能特点以及应用范围。

• the modern advanced metallurgy casting, management and information are important content of modern scale production of high chrome white cast iron grinding ball.

  现代先进的冶金铸造技术、现代管理和信息技术是更好地实现高铬白口铸铁磨球的现代规模化生产的重要内容。

• the paper describes the forging properties of white cast iron and the effect of forging ratio on the structure and properties of white cast iron.

  叙述了白口铸铁锻造工艺特点，以及锻造比对白口铸铁组织和力学性能的影响。

• the surface of the hypoeutectic white cast iron of great wearable work piece in common use was treated by laser hardening.

  对要求高耐磨的大型工件常用的亚共晶白口铸铁材料进行了不同条件的激光表面强化处理。

• using the finite element method, a mathematical model of temperature field for weld-repaired zone of white cast iron is constructed, and temperature field and heat cycle are analyzed.

  应用有限元方法建立了白口铸铁焊接接头焊补温度场的数学模型，对白口铸铁焊补温度场和热循环进行了分析。

• the corrosion wear resistance of low chromium white cast iron increases when the silicon content increases in it.

  而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。

• the spheroidizing grow, in isothermal spheroidizing process, of carbides formed from deformation under high temperature in, hypoeutectic white cast iron is studied.

  对亚共晶白口铸铁经高温形变后所获得的碳化物在等温球化过程中球化长大进行了研究。

• the current status of research work, production technique and application on high chromium white cast iron are introduced and its research trend is also discussed.

  介绍了高铬白口铸铁的研究、生产工艺和应用情况；并对高铬白口铸铁的研究方向提出了看法。

• as the result of thermal cycles, the structral components of white cast iron became cementite plus twin martensite with high hardness and high impact toughness.

  经高峰温热循环作用后，白口铸铁的组织主要为渗碳体加孪晶马氏体，其硬度高，沖击韧性较好；

• the rockwell (hrc) hardness of the white cast iron is obviously increased by complexly modifying compared with the corresponding cast iron without modification.

  白口铸铁经复合变质处理后，其洛氏（hrc）硬度比变质前有明显提高。

• using a high frequency induction furnace, the effects of brazing temperature ( t ), brazing time ( t ) and cooling speed ( v ) on microstructure and property of white cast iron have been studied.

  利用高频感应加热炉，通过改变钎焊温度、钎焊时间和冷却速度，研究了白口铸铁的组织和性能变化规律。

• the hardness and its microhardness of medium phosphorus white cast iron are higher than those of the common white cast iron, but its impact toughness slightly decreases.

  中磷白口铸铁的宏观硬度和显微硬度高于普通白口铸铁，但沖击韧性略有降低。

• the influences of different microstructure, silicon content, quenching temperature and cooling rate of the sicr white cast iron on its abrasive wear performance were investigated.

  研究了硅铬白口铸铁不同组织、不同含硅量、不同淬火加热温度及冷却速度对其耐磨粒磨损性能的影响。